Increased healthy osteoblast to osteosarcoma density ratios on specific PLGA nanopatterns
Authors Wang Y, Zhang L, Sun L, Webster T
Received 27 July 2012
Accepted for publication 24 September 2012
Published 7 January 2013 Volume 2013:8(1) Pages 159—166
DOI https://doi.org/10.2147/IJN.S36408
Checked for plagiarism Yes
Review by Single anonymous peer review
Peer reviewer comments 3
Yongchen Wang,1 Lijuan Zhang,1 Linlin Sun,2 Thomas J Webster2,3
1Department of Chemistry, 2School of Engineering, 3Department of Orthopedics, Brown University, Providence, RI, USA
Abstract: Poly(lactic-co-glycolic acid) ([PLGA] 50:50 wt% PLA:PGA) films with a flat surface and with 27 nm, 190 nm, 300 nm, 400 nm, and 520 nm nanopatterns were fabricated using a cast-mold process. The nanopatterns were transferred from self-assembled polystyrene (PS) beads to PLGA films through polydimethylsiloxane (PDMS) molds. The surface features, root-mean-square (RMS) roughness, and wettability of these PLGA surface features were studied by atomic force microscope (AFM) height scans, AFM z-sensor scans, and water contact angles, respectively. In order to evaluate the influence of the material topography alone (without changes in chemistry) for bone-cancer applications, both human healthy osteoblasts and human cancerous osteosarcoma cells were cultured on these PLGA surface features, and their densities were determined. Most importantly, compared to all other substrates, it was found that the 27 nm PLGA nanopatterns significantly increased the healthy osteoblast-to-osteosarcoma cell-density ratio. For these reasons, and since previous studies have highlighted that similar nanometer PLGA surface features decreased functions of other types of cancerous cells (specifically lung and breast), this study suggests that 27 nm PLGA nanopatterns should be further studied for a wide range of bone-cancer applications, particularly where healthy bone-cell functions need to be promoted over cancerous bone-cell functions.
Keywords: polymers, cancer, anti-cancer, surface nanometer features, bone, surface wettability
© 2013 The Author(s). This work is published and licensed by Dove Medical Press Limited. The
full terms of this license are available at https://www.dovepress.com/terms.php
and incorporate the Creative Commons Attribution
- Non Commercial (unported, v3.0) License.
By accessing the work you hereby accept the Terms. Non-commercial uses of the work are permitted
without any further permission from Dove Medical Press Limited, provided the work is properly
attributed. For permission for commercial use of this work, please see paragraphs 4.2 and 5 of our Terms.